Eu3+ doped LaAlO3 nanophosphors were successfully synthesized by a combustion process using concentrated solution of lanthanum nitrates and aluminate as oxidiser, and glycine acid as fuel. The powders were characterized by infrared spectroscopy (IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and fluorescence spectroscopy. Pure LaAlO3 phase was obtained at 800 C heated for 4 h, without formation of any intermediate phase, with an average crystal size, as determined by TEM, of 60 nm. Intense photoluminescence emission is reported at 616 nm, allowing the use of this material as red phosphor.

Combustion synthesis and photoluminescence of Eu3+ doped LaAlO3 nanophosphors

BENEDETTI, Alvise;F. Enrichi;
2012-01-01

Abstract

Eu3+ doped LaAlO3 nanophosphors were successfully synthesized by a combustion process using concentrated solution of lanthanum nitrates and aluminate as oxidiser, and glycine acid as fuel. The powders were characterized by infrared spectroscopy (IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and fluorescence spectroscopy. Pure LaAlO3 phase was obtained at 800 C heated for 4 h, without formation of any intermediate phase, with an average crystal size, as determined by TEM, of 60 nm. Intense photoluminescence emission is reported at 616 nm, allowing the use of this material as red phosphor.
2012
34
File in questo prodotto:
File Dimensione Formato  
OpticalMat2012.pdf

non disponibili

Tipologia: Documento in Pre-print
Licenza: Accesso chiuso-personale
Dimensione 1.21 MB
Formato Adobe PDF
1.21 MB Adobe PDF   Visualizza/Apri

I documenti in ARCA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10278/34411
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 32
  • ???jsp.display-item.citation.isi??? 28
social impact